| Designation | Cu-ETP |
| Min copper content | 99.9 % |
| Max electrical resistivity et 20°C | 1.7241 µΩ.cm (100%I ACS) or 0.017241 Ω mm2/m (100%I ACS) |
| Mechanical resistance | 200 mini Mpa |
| Aluminum wire according to EN 1715-2 | 1370 |
| Temper | R16 (> 160 N / mm²) |
| Maximum electrical resistivity at 20 ° C | 2.801 μΩ.cm |
| Conductivity | 61.5% IACS |
| Operating temperature | -50 ° C to + 100 ° |
| Short temperature withstand | 150 ° C |
| Designation | Cu-ETP |
| Min. copper content | 99.9 % |
| Max. electrical resistivity at 20°C (annealed state) | 1.7241 µΩ.cm (100%I ACS) |
| Mechanical strength | 200 mini Mpa |
| Metallurgical state | Annealed (State 0) |
| Designation | Cu-ETP |
| Min. copper content | 99.9 % |
| Max. electrical resistivity at 20°C (annealed state) | 1.7241 µΩ.cm (100%I ACS) |
| Mechanical strength | 200 Mpa mini |
| Metallurgical state | Annealed (State 0) |
| Wires | |
|---|---|
| Description | Cu-ETP |
| Minimum copper Content | 99.9 % |
| Max-electrical resistivity at 20°C (annealed) | 1.7241 μΩ.cm ( 100%I ACS ) |
| Metallurgical state | Annealed |
| Tubes | |
| Description | Cu-DHP |
| Minimum copper Content | 99.85 % |
| Annealed before crimping | 200 Mpa mini |
| Designation | Cu-ETP |
| Min. copper content | 99.9 % |
| Max. electrical resistivity at 20°C (annealed state) | 1.7241 µΩ.cm (100%I ACS) |
| Mechanical strength | 200 Mpa mini |
| Metallurgical state | Annealed (State 0) |
| Характеристика | Изпълнение |
|---|---|
| Материал на перките | Cu-ETP |
| Съдържание на мед | най-малко 99,9 % |
| Стандартни сечения | 10, 16, 25, 35 мм² |
| Диаметър на телта | 0,20 мм, по избор 0,10 мм |
| Разстояние между отворите | 100, 150, 200, 250, 300, 400 mm |
| Диаметър на отвора | от 5,5 до 12,5 мм |
| Специфично съпротивление при 20 °C | максимум 1,7241 µΩ cm |
| Механична якост | най-малко 200 МПа |
| Стандарт за материали | NF EN 13602 |