Grösse in mm | Durchmesser vor dem Schrumpfen | Durchmesser nach dem Schrumpfen | Wandstärke in mm | Wandstärke Innenkleber in mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Size in mm | Diameter before shrinking | Diameter after shrinking | Wall thickness in mm | Wall thickness inner adhesive in mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Tamaño en mm | Diámetro antes de la contracción | Diámetro después de la contracción | Espesor de pared en mm | Espesor de la pared del adhesivo interior en mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Rozmiar w mm | Średnica przed obkurczeniem | Średnica po obkurczeniu | Grubość ścianki w mm | Grubość ścianki kleju wewnętrznego w mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Taille en mm | Diamètre avant rétraction | Diamètre après rétraction | Épaisseur de paroi en mm | Épaisseur de paroi de la colle intérieure en mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Dimensioni in mm | Diametro prima del restringimento | Diametro dopo il restringimento | Spessore della parete in mm | Spessore della parete dell'adesivo interno in mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
الحجم في مم | القطر قبل الانكماش | القطر بعد تقلص | سمك الجدار في مم | سمك الجدار لاصق داخلي في مم |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
크기 (mm) | 수축 전의 지름 | 수축 후 직경 | 벽 두께 (mm) | 벽두께의 내부 접착제 (mm) |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
サイズ(mm | 収縮前の直径 | 収縮後の直径 | 肉厚 mm | 内側接着剤の肉厚(mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
尺寸单位:毫米 | 收缩前直径 | 收缩后直径 | 壁厚(毫米) | 壁厚内粘合剂(mm) |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Velikost v mm | Průměr před zmršením | Průměr po smršťování | Tloušťka stěny v mm | Vnitřní lepidlo s tloušťkou stěny v mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Tamanho em mm | Diâmetro antes do encolhimento | Diâmetro após retração | Espessura da parede em mm | Espessura da parede do adesivo interior em mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Размер в мм | Диаметр до усадки | Диаметр после усадки | Толщина стенки в мм | Толщина стенки внутреннего клея в мм |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Mm sayısında boyut | Küçülmeden önce çap | Küçüldükten sonra çap | Duvar kalınlığı mm | Duvar kalınlığı iç yapıştırıcı mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
MH-ben | Iameter csökkenés előtt | Iameter csökkenés után | Minden vastagság mm-ben | Fal vastagságú belső ragasztóanyag mm-ben |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
اندازه به میلی متر | قطر قبل از کوچک شدن | قطر بعد از کوچک شدن | ضخامت دیواره به میلی متر | ضخامت دیواره چسب داخلی به میلی متر |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Grootte in mm | Diameter voor krimpen | Diameter na krimpen | Wanddikte in mm | Wanddikte van binnenlijm in mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Dimensiune în mm | Diametrul înainte de contracție | Diametrul după contracție | Grosimea peretelui în mm | Grosimea peretelui adezivului interior în mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Koko mm | Halkaisija ennen kutistamista | Halkaisija kutistamisen jälkeen | Seinämän paksuus mm | Sisäisen liiman seinämän paksuus mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Veľkosť v mm | Priemer pred zmenšením | Priemer po zmenšení | Hrúbka steny v mm | Hrúbka steny vnútorného lepidla v mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Størrelse i mm | Diameter før krympning | Diameter efter krympning | Vægtykkelse i mm | Vægtykkelse af indre klæbemiddel i mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Μέγεθος σε mm | Διάμετρος πριν από τη συρρίκνωση | Διάμετρος μετά τη συρρίκνωση | Πάχος τοιχώματος σε mm | Πάχος τοιχώματος της εσωτερικής κόλλας σε mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Размер в мм | Диаметър преди свиване | Диаметър след свиване | Дебелина на стената в mm | Дебелина на стената на вътрешното лепило в mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Storlek i mm | Diameter före krympning | Diameter efter krympning | Väggtjocklek i mm | Väggtjocklek på det inre limmet i mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Velikost v mm | Premer pred krčenjem | Premer po krčenju | Debelina stene v mm | Debelina stene notranjega lepila v mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Suurus millimeetrites | Läbimõõt enne kahanemist | Läbimõõt pärast kahanemist | Seina paksus millimeetrites | Sisemise liimi seina paksus millimeetrites |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Dydis mm | Skersmuo prieš susitraukimą | Skersmuo po susitraukimo | Sienelės storis mm | Vidinių klijų sienelių storis, mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Izmērs mm | Diametrs pirms saraušanas | Diametrs pēc saraušanas | Sienas biezums mm | Iekšējās līmes sienas biezums mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Grösse in mm | Durchmesser vor dem Schrumpfen | Durchmesser nach dem Schrumpfen | Wandstärke in mm | Wandstärke Innenkleber in mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Grösse in mm | Durchmesser vor dem Schrumpfen | Durchmesser nach dem Schrumpfen | Wandstärke in mm | Wandstärke Innenkleber in mm |
3-1 | 3.0 | 1.0 | 0.90 | 0.40 |
6-2 | 6.0 | 2.0 | 1.25 | 0.45 |
9-3 | 9.0 | 3.0 | 1.45 | 0.50 |
12-4 | 12.0 | 4.0 | 1.65 | 0.50 |
19-6 | 19.0 | 6.0 | 1.95 | 0.60 |
24-8 | 24.0 | 8.0 | 2.00 | 0.60 |
40-13 | 40.0 | 13.0 | 2.45 | 0.60 |
Grösse in mm | Durchmesser vor dem Schrumpfen | Durchmesser nach dem Schrumpfen | Wandstärke in mm | Wandstärke Innenkleber |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Size in mm | Diameter before shrinking | Diameter after shrinking | Wall thickness in mm | Wall thickness inside adhesive |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Tamaño en mm | Diámetro antes de la contracción | Diámetro después de la contracción | Espesor de pared en mm | Grosor de la pared interior adhesiva |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Rozmiar w mm | Średnica przed obkurczeniem | Średnica po obkurczeniu | Grubość ścianki w mm | Grubość ścianki wewnątrz kleju |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Taille en mm | Diamètre avant rétraction | Diamètre après rétraction | Épaisseur de paroi en mm | Épaisseur de paroi de l'adhésif intérieur |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Dimensioni in mm | Diametro prima del restringimento | Diametro dopo il restringimento | Spessore della parete in mm | Spessore della parete all'interno dell'adesivo |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
الحجم في مم | القطر قبل الانكماش | القطر بعد تقلص | سمك الجدار في مم | سمك الجدار داخل لاصق |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
크기 (mm) | 수축 전의 지름 | 수축 후 직경 | 벽 두께 (mm) | 접착제 내부 벽두께 |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
サイズ(mm | 収縮前の直径 | 収縮後の直径 | 肉厚 mm | 接着剤内部の肉厚 |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
尺寸单位:毫米 | 收缩前直径 | 收缩后直径 | 壁厚(毫米) | 粘合剂内壁厚 |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Velikost v mm | Průměr před zmršením | Průměr po smršťování | Tloušťka stěny v mm | Tloušťka stěny vnitřního lepidla |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Tamanho em mm | Diâmetro antes do encolhimento | Diâmetro após retração | Espessura da parede em mm | Espessura da parede no interior do adesivo |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Размер в мм | Диаметр до усадки | Диаметр после усадки | Толщина стенки в мм | Толщина стенки внутри клея |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Mm sayısında boyut | Küçülmeden önce çap | Küçüldükten sonra çap | Duvar kalınlığı mm | İç duvar kalınlığı yapıştırıcı |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
MH-ben | Iameter csökkenés előtt | Iameter csökkenés után | Minden vastagság mm-ben | Fal vastagsága ragasztóra belül |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
اندازه به میلی متر | قطر قبل از کوچک شدن | قطر بعد از کوچک شدن | ضخامت دیواره به میلی متر | ضخامت دیواره داخل چسب |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Grootte in mm | Diameter voor krimpen | Diameter na krimpen | Wanddikte in mm | Wanddikte binnen lijm |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Dimensiune în mm | Diametrul înainte de contracție | Diametrul după contracție | Grosimea peretelui în mm | Grosimea peretelui în interiorul adezivului |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Koko mm | Halkaisija ennen kutistamista | Halkaisija kutistamisen jälkeen | Seinämän paksuus mm | Seinämän paksuus liiman sisäpuolella |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Veľkosť v mm | Priemer pred zmenšením | Priemer po zmenšení | Hrúbka steny v mm | Hrúbka steny vo vnútri lepidla |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Størrelse i mm | Diameter før krympning | Diameter efter krympning | Vægtykkelse i mm | Vægtykkelse inden i klæbemidlet |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Μέγεθος σε mm | Διάμετρος πριν από τη συρρίκνωση | Διάμετρος μετά τη συρρίκνωση | Πάχος τοιχώματος σε mm | Πάχος τοιχώματος μέσα στην κόλλα |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Размер в мм | Диаметър преди свиване | Диаметър след свиване | Дебелина на стената в mm | Дебелина на стената вътре в лепилото |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Storlek i mm | Diameter före krympning | Diameter efter krympning | Väggtjocklek i mm | Väggtjocklek på insidan av limmet |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Velikost v mm | Premer pred krčenjem | Premer po krčenju | Debelina stene v mm | Debelina stene znotraj lepila |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Suurus millimeetrites | Läbimõõt enne kahanemist | Läbimõõt pärast kahanemist | Seina paksus millimeetrites | Seina paksus liimi sees |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Dydis mm | Skersmuo prieš susitraukimą | Skersmuo po susitraukimo | Sienelės storis mm | Sienelės storis klijų viduje |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Izmērs mm | Diametrs pirms saraušanas | Diametrs pēc saraušanas | Sienas biezums mm | Sienas biezums līmes iekšpusē |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Grösse in mm | Durchmesser vor dem Schrumpfen | Durchmesser nach dem Schrumpfen | Wandstärke in mm | Wandstärke Innenkleber |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Grösse in mm | Durchmesser vor dem Schrumpfen | Durchmesser nach dem Schrumpfen | Wandstärke in mm | Wandstärke Innenkleber |
4-1 | 4.0 | 1.0 | 1.05 | 0.50 |
8-2 | 8.0 | 2.0 | 1.55 | 0.60 |
12-3 | 12.0 | 3.0 | 1.75 | 0.60 |
16-4 | 16.0 | 4.0 | 2.00 | 0.70 |
24-6 | 24.0 | 6.0 | 2.60 | 0.75 |
32-8 | 32.0 | 8.0 | 3.00 | 0.90 |
52-13 | 52.0 | 13.0 | 3.35 | 0.95 |
Eigenschaft | Wert |
Material | Polyolefin |
Wandung | dünnwandig |
Kleber | mit Innenkleber |
Schrumpfverhältnis | 3 : 1 |
Schrumpftemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Zugfestigkeit | 12 |
Bruchdehnung (%) | 300 |
Längenänderung | – 8 % max. |
Durchschlagfestigkeit | 15 kV / mm |
Spezifischer Widerstand (Ohm x cm) | 10^14 |
Feature | Value |
Material | Polyolefin |
Wall | thin-walled |
Glue | with inside adhesive |
Shrinkage ratio | 3 : 1 |
Shrink temperature (min.) | 120°C |
Continuous operating temperature | -55 ºC - +125 ºC |
Tensile strength | 12 |
Elongation at break (%) | 300 |
Length change | – 8 % max. |
Dielectric strength | 15 kV / mm |
Specific resistance (Ohm x cm) | 10^14 |
Característica | Valor |
Material | Poliolefina |
Pared | Paredes finas |
Pegamento | con adhesivo interno |
Índice de contracción | 3 : 1 |
Temperatura de retracción (mín.) | 120°C |
Temperatura de funcionamiento continuo | -55 ºC - +125 ºC |
Resistencia a la tracción | 12 |
Alargamiento a la rotura (%) | 300 |
Cambio de longitud | – 8 % max. |
Rigidez dieléctrica | 15 kV / mm |
Resistencia específica (Ohm x cm) | 10^14 |
Cecha | Wartość |
Materiał | Poliolefina |
Ściana | Cienkościenne |
Klej | z wewnętrznym klejem |
Współczynnik skurczu | 3 : 1 |
Temperatura obkurczania (min.) | 120°C |
Temperatura pracy ciągłej | -55 ºC - +125 ºC |
Wytrzymałość na rozciąganie | 12 |
Wydłużenie przy zerwaniu (%) | 300 |
Zmiana długości | – 8 % max. |
Wytrzymałość dielektryczna | 15 kV / mm |
Opór właściwy (Ohm x cm) | 10^14 |
Propriété | Valeur |
Matériau | Polyoléfine |
Paroi | à paroi mince |
Colle | avec adhésif intérieur |
Rapport de rétraction | 3 : 1 |
Température de rétraction (min.) | 120°C |
Température de fonctionnement continu | -55 ºC - +125 ºC |
Résistance à la traction | 12 |
Allongement à la rupture (%) | 300 |
Changement de longueur | – 8 % max. |
Rigidité diélectrique | 15 kV / mm |
Résistance spécifique (Ohm x cm) | 10^14 |
Caratteristica | Valore |
Materiale | Poliolefina |
Muro | A parete sottile |
Colla | con adesivo interno |
Rapporto di restringimento | 3 : 1 |
Temperatura di restringimento (min.) | 120°C |
Temperatura di esercizio continua | -55 ºC - +125 ºC |
Resistenza alla trazione | 12 |
Allungamento a rottura (%) | 300 |
Variazione della lunghezza | – 8 % max. |
Rigidità dielettrica | 15 kV / mm |
Resistenza specifica (Ohm x cm) | 10^14 |
الميزة | القيمة |
المواد | البولي أوليفين |
الحائط | رقيقة الجدران |
الغراء | مع لاصق داخل |
نسبة الانكماش | 3 : 1 |
تقلص درجة الحرارة (دقيقة) | 120°C |
درجة حرارة التشغيل المستمرة | -55 ºC - +125 ºC |
قوة الشد | 12 |
استطالة عند الكسر (٪) | 300 |
تغيير الطول | – 8 % max. |
قوة عازل | 15 kV / mm |
مقاومة محددة (أوم × سم) | 10^14 |
특징 | 값 |
재료 | 폴리올레핀 |
벽 | 얇은 벽 |
접착제 | 내부 접착제가 있습니다. |
수축률 | 3 : 1 |
수축 온도(min.) | 120°C |
연속 작동 온도 | -55 ºC - +125 ºC |
인장 강도 | 12 |
파손시 신장(%) | 300 |
길이 변경 | – 8 % max. |
유전체 강도 | 15 kV / mm |
비저항 Ohm x cm | 10^14 |
特徴 | 価値 |
素材 | ポリオレフィン |
壁 | 薄肉 |
接着剤 | 内部接着剤付き |
収縮率 | 3 : 1 |
収縮温度(最低) | 120°C |
連続使用温度 | -55 ºC - +125 ºC |
引張強さ | 12 |
破断伸度(%) | 300 |
長さの変化 | – 8 % max. |
絶縁耐力 | 15 kV / mm |
比抵抗(オーム×cm) | 10^14 |
特征 | 价值 |
材料 | 聚烯烃 |
墙 | 薄壁的 |
胶合 | 带内胶 |
收缩率 | 3 : 1 |
收缩温度(最小值) | 120°C |
连续工作温度 | -55 ºC - +125 ºC |
抗拉强度 | 12 |
断裂伸长率(%) | 300 |
长度变化 | – 8 % max. |
介电强度 | 15 kV / mm |
比电阻(欧姆×厘米) | 10^14 |
Funkce? | Hodnota? |
Materiál? | Polyolefin |
Zdi? | Tenkostěnná |
Plepidlo? | Vnitřní lepidlo |
Poměr smršťování | 3 : 1 |
Teplota smršťování (min.) | 120°C |
Kontinuální provozní teplota | -55 ºC - +125 ºC |
Pevnost v tahu | 12 |
Prodloužení při přerušení (%) | 300 |
Změna délky | – 8 % max. |
Dielektrická pevnost | 15 kV / mm |
Specifický odpor (Ohm x cm) | 10^14 |
Característica | Valor |
Material | Poliolefina |
Parede | Paredes finas |
Cola | com adesivo interno |
Rácio de retração | 3 : 1 |
Temperatura de retração (min.) | 120°C |
Temperatura de funcionamento contínuo | -55 ºC - +125 ºC |
Resistência à tração | 12 |
Alongamento na rutura (%) | 300 |
Alteração do comprimento | – 8 % max. |
Resistência dieléctrica | 15 kV / mm |
Resistência específica (Ohm x cm) | 10^14 |
Характеристика | Значение |
Материал | Полиолефин |
Стена | Тонкостенные |
Клей | с внутренним клеем |
Коэффициент усадки | 3 : 1 |
Температура усадки (мин.) | 120°C |
Непрерывная рабочая температура | -55 ºC - +125 ºC |
Прочность на разрыв | 12 |
Удлинение при разрыве (%) | 300 |
Изменение длины | – 8 % max. |
Диэлектрическая прочность | 15 kV / mm |
Удельное сопротивление (Ом х см) | 10^14 |
Özellik | Değer |
Malzeme | Poliolefin |
Duvarlar | Ince duvarlı |
Tutkal | İç yapıştırıcı ile |
Büzülme oranı | 3 : 1 |
Sıcaklık daralma (min.) | 120°C |
Sürekli çalışma sıcaklığı | -55 ºC - +125 ºC |
Çekme mukavemeti | 12 |
Kırılma uzaması (%) | 300 |
Uzun değişikliği | – 8 % max. |
Dielektrik mukavemet | 15 kV / mm |
Spesifik direnç (Ohm x cm) | 10^14 |
Eature | AlueCity in Alberta Canada |
AZ ANYAK | Oliolefin |
Minden | Vágfalú |
Lue | Belső ragasztóval |
Hrinkage arány | 3 : 1 |
Hrink hőmérséklete (minimum) | 120°C |
A folyamatos üzemi hőmérséklet | -55 ºC - +125 ºC |
Szilára erősség | 12 |
Hosszúság szünetelés (%) | 300 |
Hosszúsági változás | – 8 % max. |
IElectric erősség | 15 kV / mm |
Specifik rezisztencia (Ohm x cm) | 10^14 |
ویژگی ها | ارزش |
مواد | پلی الیفین |
دیوار | دیواره نازک |
چسب ؟ | با چسب داخلی |
نسبت انقباض | 3 : 1 |
دمای کوچک شدن (دقیق) | 120°C |
دمای کار مداوم | -55 ºC - +125 ºC |
مقاومت کششی | 12 |
کشیدگی در زمان شکستن (٪) | 300 |
تغییر طول | – 8 % max. |
مقاومت دی الکتریک | 15 kV / mm |
مقاومت خاص (هم x سانتی متر) | 10^14 |
Functie | Waarde |
Materiaal | Polyolefine |
Muur | Dunwandig |
Lijm | met interne lijm |
Krimpverhouding | 3 : 1 |
Krimptemperatuur (min.) | 120°C |
Continue bedrijfstemperatuur | -55 ºC - +125 ºC |
Treksterkte | 12 |
Rek bij breuk (%) | 300 |
Lengteverandering | – 8 % max. |
Diëlektrische sterkte | 15 kV / mm |
Specifieke weerstand (Ohm x cm) | 10^14 |
Caracteristică | Valoare |
Material | Poliolefină |
Perete | Cu pereți subțiri |
Lipici | cu adeziv intern |
Raportul de contracție | 3 : 1 |
Temperatura de contracție (min.) | 120°C |
Temperatura de funcționare continuă | -55 ºC - +125 ºC |
Rezistența la tracțiune | 12 |
Alungirea la rupere (%) | 300 |
Schimbare de lungime | – 8 % max. |
Rezistența dielectrică | 15 kV / mm |
Rezistența specifică (Ohm x cm) | 10^14 |
Ominaisuus | Arvo |
Materiaali | Polyolefiini |
Seinä | Ohutseinäiset |
Liima | sisäisellä liimalla |
Kutistumissuhde | 3 : 1 |
Kutistumislämpötila (min.) | 120°C |
Jatkuva käyttölämpötila | -55 ºC - +125 ºC |
Vetolujuus | 12 |
Murtovenymä (%) | 300 |
Pituuden muutos | – 8 % max. |
Dielektrinen lujuus | 15 kV / mm |
Ominaisvastus (Ohm x cm) | 10^14 |
Funkcia | Hodnota |
Materiál | Polyolefín |
Stena | Tenkostenné |
Lepidlo | s vnútorným lepidlom |
Pomer zmrštenia | 3 : 1 |
Teplota zmršťovania (min.) | 120°C |
Trvalá prevádzková teplota | -55 ºC - +125 ºC |
Pevnosť v ťahu | 12 |
Predĺženie pri pretrhnutí (%) | 300 |
Zmena dĺžky | – 8 % max. |
Dielektrická pevnosť | 15 kV / mm |
Špecifický odpor (Ohm x cm) | 10^14 |
Funktion | Værdi |
Materiale | Polyolefin |
Væg | Tyndvægget |
Lim | med indvendigt klæbemiddel |
Krympningsgrad | 3 : 1 |
Krympetemperatur (min.) | 120°C |
Kontinuerlig driftstemperatur | -55 ºC - +125 ºC |
Trækstyrke | 12 |
Forlængelse ved brud (%) | 300 |
Ændring af længde | – 8 % max. |
Dielektrisk styrke | 15 kV / mm |
Specifik modstand (Ohm x cm) | 10^14 |
Χαρακτηριστικό γνώρισμα | Αξία |
Υλικό | Πολυολεφίνη |
Τοίχος | Λεπτότοιχα |
Κόλλα | με εσωτερική κόλλα |
Αναλογία συρρίκνωσης | 3 : 1 |
Θερμοκρασία συρρίκνωσης (min.) | 120°C |
Συνεχής θερμοκρασία λειτουργίας | -55 ºC - +125 ºC |
Αντοχή σε εφελκυσμό | 12 |
Επιμήκυνση κατά τη θραύση (%) | 300 |
Αλλαγή μήκους | – 8 % max. |
Διηλεκτρική αντοχή | 15 kV / mm |
Ειδική αντίσταση (Ohm x cm) | 10^14 |
Функции | Стойност |
Материал | Полиолефин |
Стена | Тънкостенни |
Лепило | с вътрешно лепило |
Коефициент на свиване | 3 : 1 |
Температура на свиване (мин.) | 120°C |
Непрекъсната работна температура | -55 ºC - +125 ºC |
Якост на опън | 12 |
Удължение при скъсване (%) | 300 |
Промяна на дължината | – 8 % max. |
Диелектрична якост | 15 kV / mm |
Специфично съпротивление (Ohm x cm) | 10^14 |
Funktion | Värde |
Material | Polyolefin |
Vägg | Tunnväggig |
Lim | med invändigt häftämne |
Krympningsgrad | 3 : 1 |
Krymptemperatur (min.) | 120°C |
Kontinuerlig driftstemperatur | -55 ºC - +125 ºC |
Draghållfasthet | 12 |
Töjning vid brott (%) | 300 |
Längdförändring | – 8 % max. |
Dielektrisk hållfasthet | 15 kV / mm |
Specifikt motstånd (Ohm x cm) | 10^14 |
Funkcija | Vrednost |
Material | Poliolefin |
Stena | Tankostenski |
Lepilo | z notranjim lepilom |
Razmerje krčenja | 3 : 1 |
Temperatura krčenja (min.) | 120°C |
Trajna delovna temperatura | -55 ºC - +125 ºC |
Natezna trdnost | 12 |
Podaljšek ob pretrgu (%) | 300 |
Sprememba dolžine | – 8 % max. |
Dielektrična trdnost | 15 kV / mm |
Specifična upornost (Ohm x cm) | 10^14 |
Funktsioon | Väärtus |
Materjal | Polüolefiin |
Seina | Õhukesed seinad |
Liim | sisemise liimiga |
Kahanemise suhe | 3 : 1 |
Kahanemistemperatuur (min.) | 120°C |
Pidev töötemperatuur | -55 ºC - +125 ºC |
Tõmbetugevus | 12 |
Pikendus murdumisel (%) | 300 |
Pikkuse muutus | – 8 % max. |
Dielektriline tugevus | 15 kV / mm |
Eritakistus (Ohm x cm) | 10^14 |
Funkcija | Vertė |
Medžiaga | Poliolefinas |
Siena | Plonasienis |
Klijai | su vidiniais klijais |
Susitraukimo santykis | 3 : 1 |
Sutraukimo temperatūra (min.) | 120°C |
Nuolatinė darbinė temperatūra | -55 ºC - +125 ºC |
Tempimo stipris | 12 |
Pailgėjimas nutrūkus (%) | 300 |
Ilgio pokytis | – 8 % max. |
Dielektrinis stipris | 15 kV / mm |
Savitoji varža (Ohm x cm) | 10^14 |
Funkcija | Vērtība |
Materiāls | Poliolefīns |
Siena | Plānsienu |
Līme | ar iekšējo līmi |
Saraušanās koeficients | 3 : 1 |
Samazināšanas temperatūra (min.) | 120°C |
Pastāvīgā darba temperatūra | -55 ºC - +125 ºC |
Stiepes izturība | 12 |
Pagarinājums pārraušanas brīdī (%) | 300 |
Garuma izmaiņas | – 8 % max. |
Dielektriskā izturība | 15 kV / mm |
Īpatnējā pretestība (Ohm x cm) | 10^14 |
Eigenschaft | Wert |
Material | Polyolefin |
Wandung | dünnwandig |
Kleber | mit Innenkleber |
Schrumpfverhältnis | 3 : 1 |
Schrumpftemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Zugfestigkeit | 12 |
Bruchdehnung (%) | 300 |
Längenänderung | – 8 % max. |
Durchschlagfestigkeit | 15 kV / mm |
Spezifischer Widerstand (Ohm x cm) | 10^14 |
Eigenschaft | Wert |
Material | Polyolefin |
Wandung | dünnwandig |
Kleber | mit Innenkleber |
Schrumpfverhältnis | 3 : 1 |
Schrumpftemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Zugfestigkeit | 12 |
Bruchdehnung (%) | 300 |
Längenänderung | – 8 % max. |
Durchschlagfestigkeit | 15 kV / mm |
Spezifischer Widerstand (Ohm x cm) | 10^14 |
Eigenschaft | Wert |
Material | Polyolefin |
Wandung | dünnwandig |
Kleber | mit Innenkleber |
Schrumpfverhältnis | 4 : 1 |
Schrumpftemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Zugfestigkeit | 12 |
Bruchdehnung (%) | 300 |
Längenänderung | – 8 % max. |
Durchschlagfestigkeit | 15 kV / mm |
Spezifischer Widerstand (Ohm x cm) | 10^14 |
Feature | Value |
Material | Polyolefin |
Wall | thin-walled |
Glue | with inside adhesive |
Shrinkage ratio | 4 : 1 |
Shrink temperature (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Tensile strength | 12 |
Elongation at break (%) | 300 |
Length change | – 8 % max. |
Dielectric strength | 15 kV / mm |
Specific resistance (Ohm x cm) | 10^14 |
Característica | Valor |
Material | Poliolefina |
Pared | Paredes finas |
Pegamento | con adhesivo interno |
Índice de contracción | 4 : 1 |
Temperatura de retracción (mín.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Resistencia a la tracción | 12 |
Alargamiento a la rotura (%) | 300 |
Cambio de longitud | – 8 % max. |
Rigidez dieléctrica | 15 kV / mm |
Resistencia específica (Ohm x cm) | 10^14 |
Cecha | Wartość |
Materiał | Poliolefina |
Ściana | Cienkościenne |
Klej | z wewnętrznym klejem |
Współczynnik skurczu | 4 : 1 |
Temperatura obkurczania (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Wytrzymałość na rozciąganie | 12 |
Wydłużenie przy zerwaniu (%) | 300 |
Zmiana długości | – 8 % max. |
Wytrzymałość dielektryczna | 15 kV / mm |
Opór właściwy (Ohm x cm) | 10^14 |
Propriété | Valeur |
Matériau | Polyoléfine |
Paroi | à paroi mince |
Colle | avec adhésif intérieur |
Rapport de rétraction | 4 : 1 |
Température de rétraction (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Résistance à la traction | 12 |
Allongement à la rupture (%) | 300 |
Changement de longueur | – 8 % max. |
Rigidité diélectrique | 15 kV / mm |
Résistance spécifique (Ohm x cm) | 10^14 |
Caratteristica | Valore |
Materiale | Poliolefina |
Muro | A parete sottile |
Colla | con adesivo interno |
Rapporto di restringimento | 4 : 1 |
Temperatura di restringimento (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Resistenza alla trazione | 12 |
Allungamento a rottura (%) | 300 |
Variazione della lunghezza | – 8 % max. |
Rigidità dielettrica | 15 kV / mm |
Resistenza specifica (Ohm x cm) | 10^14 |
الميزة | القيمة |
المواد | البولي أوليفين |
الحائط | رقيقة الجدران |
الغراء | مع لاصق داخل |
نسبة الانكماش | 4 : 1 |
تقلص درجة الحرارة (دقيقة) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
قوة الشد | 12 |
استطالة عند الكسر (٪) | 300 |
تغيير الطول | – 8 % max. |
قوة عازل | 15 kV / mm |
مقاومة محددة (أوم × سم) | 10^14 |
특징 | 값 |
재료 | 폴리올레핀 |
벽 | 얇은 벽 |
접착제 | 내부 접착제가 있습니다. |
수축률 | 4 : 1 |
수축 온도(min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
인장 강도 | 12 |
파손시 신장(%) | 300 |
길이 변경 | – 8 % max. |
유전체 강도 | 15 kV / mm |
비저항 Ohm x cm | 10^14 |
特徴 | 価値 |
素材 | ポリオレフィン |
壁 | 薄肉 |
接着剤 | 内部接着剤付き |
収縮率 | 4 : 1 |
収縮温度(最低) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
引張強さ | 12 |
破断伸度(%) | 300 |
長さの変化 | – 8 % max. |
絶縁耐力 | 15 kV / mm |
比抵抗(オーム×cm) | 10^14 |
特征 | 价值 |
材料 | 聚烯烃 |
墙 | 薄壁的 |
胶合 | 带内胶 |
收缩率 | 4 : 1 |
收缩温度(最小值) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
抗拉强度 | 12 |
断裂伸长率(%) | 300 |
长度变化 | – 8 % max. |
介电强度 | 15 kV / mm |
比电阻(欧姆×厘米) | 10^14 |
Funkce? | Hodnota? |
Materiál? | Polyolefin |
Zdi? | Tenkostěnná |
Plepidlo? | Vnitřní lepidlo |
Poměr smršťování | 4 : 1 |
Teplota smršťování (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Pevnost v tahu | 12 |
Prodloužení při přerušení (%) | 300 |
Změna délky | – 8 % max. |
Dielektrická pevnost | 15 kV / mm |
Specifický odpor (Ohm x cm) | 10^14 |
Característica | Valor |
Material | Poliolefina |
Parede | Paredes finas |
Cola | com adesivo interno |
Rácio de retração | 4 : 1 |
Temperatura de retração (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Resistência à tração | 12 |
Alongamento na rutura (%) | 300 |
Alteração do comprimento | – 8 % max. |
Resistência dieléctrica | 15 kV / mm |
Resistência específica (Ohm x cm) | 10^14 |
Характеристика | Значение |
Материал | Полиолефин |
Стена | Тонкостенные |
Клей | с внутренним клеем |
Коэффициент усадки | 4 : 1 |
Температура усадки (мин.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Прочность на разрыв | 12 |
Удлинение при разрыве (%) | 300 |
Изменение длины | – 8 % max. |
Диэлектрическая прочность | 15 kV / mm |
Удельное сопротивление (Ом х см) | 10^14 |
Özellik | Değer |
Malzeme | Poliolefin |
Duvarlar | Ince duvarlı |
Tutkal | İç yapıştırıcı ile |
Büzülme oranı | 4 : 1 |
Sıcaklık daralma (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Çekme mukavemeti | 12 |
Kırılma uzaması (%) | 300 |
Uzun değişikliği | – 8 % max. |
Dielektrik mukavemet | 15 kV / mm |
Spesifik direnç (Ohm x cm) | 10^14 |
Eature | AlueCity in Alberta Canada |
AZ ANYAK | Oliolefin |
Minden | Vágfalú |
Lue | Belső ragasztóval |
Hrinkage arány | 4 : 1 |
Hrink hőmérséklete (minimum) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Szilára erősség | 12 |
Hosszúság szünetelés (%) | 300 |
Hosszúsági változás | – 8 % max. |
IElectric erősség | 15 kV / mm |
Specifik rezisztencia (Ohm x cm) | 10^14 |
ویژگی ها | ارزش |
مواد | پلی الیفین |
دیوار | دیواره نازک |
چسب ؟ | با چسب داخلی |
نسبت انقباض | 4 : 1 |
دمای کوچک شدن (دقیق) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
مقاومت کششی | 12 |
کشیدگی در زمان شکستن (٪) | 300 |
تغییر طول | – 8 % max. |
مقاومت دی الکتریک | 15 kV / mm |
مقاومت خاص (هم x سانتی متر) | 10^14 |
Functie | Waarde |
Materiaal | Polyolefine |
Muur | Dunwandig |
Lijm | met interne lijm |
Krimpverhouding | 4 : 1 |
Krimptemperatuur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Treksterkte | 12 |
Rek bij breuk (%) | 300 |
Lengteverandering | – 8 % max. |
Diëlektrische sterkte | 15 kV / mm |
Specifieke weerstand (Ohm x cm) | 10^14 |
Caracteristică | Valoare |
Material | Poliolefină |
Perete | Cu pereți subțiri |
Lipici | cu adeziv intern |
Raportul de contracție | 4 : 1 |
Temperatura de contracție (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Rezistența la tracțiune | 12 |
Alungirea la rupere (%) | 300 |
Schimbare de lungime | – 8 % max. |
Rezistența dielectrică | 15 kV / mm |
Rezistența specifică (Ohm x cm) | 10^14 |
Ominaisuus | Arvo |
Materiaali | Polyolefiini |
Seinä | Ohutseinäiset |
Liima | sisäisellä liimalla |
Kutistumissuhde | 4 : 1 |
Kutistumislämpötila (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Vetolujuus | 12 |
Murtovenymä (%) | 300 |
Pituuden muutos | – 8 % max. |
Dielektrinen lujuus | 15 kV / mm |
Ominaisvastus (Ohm x cm) | 10^14 |
Funkcia | Hodnota |
Materiál | Polyolefín |
Stena | Tenkostenné |
Lepidlo | s vnútorným lepidlom |
Pomer zmrštenia | 4 : 1 |
Teplota zmršťovania (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Pevnosť v ťahu | 12 |
Predĺženie pri pretrhnutí (%) | 300 |
Zmena dĺžky | – 8 % max. |
Dielektrická pevnosť | 15 kV / mm |
Špecifický odpor (Ohm x cm) | 10^14 |
Funktion | Værdi |
Materiale | Polyolefin |
Væg | Tyndvægget |
Lim | med indvendigt klæbemiddel |
Krympningsgrad | 4 : 1 |
Krympetemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Trækstyrke | 12 |
Forlængelse ved brud (%) | 300 |
Ændring af længde | – 8 % max. |
Dielektrisk styrke | 15 kV / mm |
Specifik modstand (Ohm x cm) | 10^14 |
Χαρακτηριστικό γνώρισμα | Αξία |
Υλικό | Πολυολεφίνη |
Τοίχος | Λεπτότοιχα |
Κόλλα | με εσωτερική κόλλα |
Αναλογία συρρίκνωσης | 4 : 1 |
Θερμοκρασία συρρίκνωσης (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Αντοχή σε εφελκυσμό | 12 |
Επιμήκυνση κατά τη θραύση (%) | 300 |
Αλλαγή μήκους | – 8 % max. |
Διηλεκτρική αντοχή | 15 kV / mm |
Ειδική αντίσταση (Ohm x cm) | 10^14 |
Функции | Стойност |
Материал | Полиолефин |
Стена | Тънкостенни |
Лепило | с вътрешно лепило |
Коефициент на свиване | 4 : 1 |
Температура на свиване (мин.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Якост на опън | 12 |
Удължение при скъсване (%) | 300 |
Промяна на дължината | – 8 % max. |
Диелектрична якост | 15 kV / mm |
Специфично съпротивление (Ohm x cm) | 10^14 |
Funktion | Värde |
Material | Polyolefin |
Vägg | Tunnväggig |
Lim | med invändigt häftämne |
Krympningsgrad | 4 : 1 |
Krymptemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Draghållfasthet | 12 |
Töjning vid brott (%) | 300 |
Längdförändring | – 8 % max. |
Dielektrisk hållfasthet | 15 kV / mm |
Specifikt motstånd (Ohm x cm) | 10^14 |
Funkcija | Vrednost |
Material | Poliolefin |
Stena | Tankostenski |
Lepilo | z notranjim lepilom |
Razmerje krčenja | 4 : 1 |
Temperatura krčenja (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Natezna trdnost | 12 |
Podaljšek ob pretrgu (%) | 300 |
Sprememba dolžine | – 8 % max. |
Dielektrična trdnost | 15 kV / mm |
Specifična upornost (Ohm x cm) | 10^14 |
Funktsioon | Väärtus |
Materjal | Polüolefiin |
Seina | Õhukesed seinad |
Liim | sisemise liimiga |
Kahanemise suhe | 4 : 1 |
Kahanemistemperatuur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Tõmbetugevus | 12 |
Pikendus murdumisel (%) | 300 |
Pikkuse muutus | – 8 % max. |
Dielektriline tugevus | 15 kV / mm |
Eritakistus (Ohm x cm) | 10^14 |
Funkcija | Vertė |
Medžiaga | Poliolefinas |
Siena | Plonasienis |
Klijai | su vidiniais klijais |
Susitraukimo santykis | 4 : 1 |
Sutraukimo temperatūra (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Tempimo stipris | 12 |
Pailgėjimas nutrūkus (%) | 300 |
Ilgio pokytis | – 8 % max. |
Dielektrinis stipris | 15 kV / mm |
Savitoji varža (Ohm x cm) | 10^14 |
Funkcija | Vērtība |
Materiāls | Poliolefīns |
Siena | Plānsienu |
Līme | ar iekšējo līmi |
Saraušanās koeficients | 4 : 1 |
Samazināšanas temperatūra (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Stiepes izturība | 12 |
Pagarinājums pārraušanas brīdī (%) | 300 |
Garuma izmaiņas | – 8 % max. |
Dielektriskā izturība | 15 kV / mm |
Īpatnējā pretestība (Ohm x cm) | 10^14 |
Eigenschaft | Wert |
Material | Polyolefin |
Wandung | dünnwandig |
Kleber | mit Innenkleber |
Schrumpfverhältnis | 4 : 1 |
Schrumpftemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Zugfestigkeit | 12 |
Bruchdehnung (%) | 300 |
Längenänderung | – 8 % max. |
Durchschlagfestigkeit | 15 kV / mm |
Spezifischer Widerstand (Ohm x cm) | 10^14 |
Eigenschaft | Wert |
Material | Polyolefin |
Wandung | dünnwandig |
Kleber | mit Innenkleber |
Schrumpfverhältnis | 4 : 1 |
Schrumpftemperatur (min.) | 120°C |
Dauerbetriebstemperatur | -55 ºC - +125 ºC |
Zugfestigkeit | 12 |
Bruchdehnung (%) | 300 |
Längenänderung | – 8 % max. |
Durchschlagfestigkeit | 15 kV / mm |
Spezifischer Widerstand (Ohm x cm) | 10^14 |